Summary of Durability Analysis of Concrete Structures

Zhenkai Zhu

doi:10.54097/exw7hs77

Authors

Zhenkai Zhu

DOI:

https://doi.org/10.54097/exw7hs77

Keywords:

Concrete; Durability; Life prediction.

Abstract

The service life of concrete is closely related to the durability of concrete structure, with the development of infrastructure construction in our country, more and more attention has been paid to the study on the durability of concrete structure. This paper mainly analyzes the relevant factors affecting the durability of concrete structures, such as sulfate corrosion, chlorine salt corrosion, steel corrosion and concrete carbonization. At the same time, this paper studies from the perspective of life prediction of concrete structure to provide some reference for durability design of concrete structure.

Downloads

Download data is not yet available.

References

LI V C. High-performance and multifunctional cement-based composite material[J]. Engineering, 2019, 5(2): 250−260.

Liu Juanhong, Ma Hongbo, Duan Pinjia, et al. Corrosion resistance of ultra-deep well wall concrete under sulfate dry-wet cycling environment[J]. Materials Herald, 2021, 35(12): 12081-12086.

Zhang Xide. Research on some problems of durability of reinforced concrete members [D]. Guangxi University, 2004.

Jin Weiliang, Zhao Yuxi, Yan Fei. Mechanism of uniform reinforcement rusting and expansion forces in reinforced concrete members[J]. Journal of Water Resources, 2001(07): 57-62.

Yao Jitao, Gu Hui, Zhang Yijiu, et al. Probabilistic design expression for carbonation durability of concrete structures[J]. Journal of Xi'an University of Architecture and Technology(Natural Science Edition),2015,47(01):1-5.

Tu Yongming, Lv Zhitao. Experimental study on carbonization of concrete under stress [J]. Journal of Southeast University (Natural Science Edition),2003(05):573-576.

Lu Limin, Xu Weihao, Wang Shouxing, et al. Experimental study on carbonization and chloride ion erosion of concrete after high temperature [J]. Concrete,2023(01):53-57+63.

Ferraris C F, Stutzman P E, Snyder K A. Sulfate resistance of concrete: a new approach[J]. R&D Serial, 2006, 2486: 301-313.

Da Chen, Yu Xiaotong, Liao Yingdi, et al. Progress of research on sulfate erosion of concrete [J]. Journal of Chongqing Jiaotong University (Natural Science Edition),2016,35(02):24-30.

Chen J, Jiang M. Long-term evolution of delayed ettringite and gypsum in Portland cement mortars under sulfate erosion[J]. Construction and Building Materials, 2009, 23(2): 812-816.

Gao Rundong, Zhao Shunbo, Li Qingbin, et al. Experimental study on the deterioration mechanism of sulfate attack on concrete under dry and wet cycle[J]. Journal of Civil Engineering, 2010, 43(02):48-54.

Liu Zanqun, Deng Dehua, Geert De Schutter, et al. "Microanalysis of sulfate crystallization damage in concrete (II)-concrete[J]. Journal of Silicates,2012,40(05):631-637.

Xing Feng, Leng Faguang, Feng Naiqian, et al. Effect of long-term continuous loading on chloride ion permeability of plain concrete[J]. Concrete,2004(05):3-8.

Jin Zuquan, Sun Wei, Zhao Tiejun, et al. Curing degree of concrete to chloride ions in different solutions[J]. Journal of Silicate,2009,37(07):1068-1072+1078.

Shi C, Shi Z, Hu X, et al. A review on alkali-aggregate reactions in alkali-activated mortars/concretes made with alkali-reactive aggregates[J]. Materials and Structures, 2015, 48: 621-628.

Yang Changhui, Pu Xincheng, Wu Fang. Study on alkali aggregate reaction expansion of alkali slag cement mortar[J]. Journal of Silicate,1999(06):651-657.

Wang Zijia. Damage of concrete structure by alkali aggregate reaction and chemical restraining measures [J]. Guangdong Chemical Industry,2023,50(18):62-63+44.

Jia Xianhua. Analysis of factors affecting freeze-thaw damage and durability test of concrete[J]. Construction Machinery, 2022(09):61-63.

Wu Haotian. Mechanism of freeze-thaw cycle failure of iron tailings concrete [D]. Liaoning Shihua University,2023.

Li Yao. Durability study and life prediction of hydraulic concrete under freeze-thaw and sulfate composite [D]. Xi'an University of Technology,2023.

Yang Dongpeng, Guo Weimin, WANG Baomin. Prediction and application of freeze-thaw damage life of concrete based on Weibull model [J]. Journal of Water Resources, 2022, 53(08): 977-983.

Lu Chenggong, Wei Zhiqiang, Qiao Hongxia, et al. Durability life prediction of reinforced concrete in underground corrosive environment based on Wiener stochastic process[J]. Journal of Hunan University (Natural Science Edition),2021,48(07):119-128.

CLIFTON J R.Prediction the service life of concrete[J].ACI Mater J,1993,90(6): 611-617.

Guan Bowen, Chen Shuanfa, Li Huaping, et al. Prediction of sulfate corrosion life of concrete under fatigue load [J]. Journal of Building Materials,2012,15(03):395-398.

Qiao Hongxia, Zhu Binrong, Lu Chenggong, et al. Accelerated life test of concrete based on Wiener stochastic process[J]. Journal of Construction Materials, 2016, 19(06): 1023-1027+1061.

Yu Hongfa, Sun Wei, Ma Haiyan, et al. Concrete life prediction method based on damage evolution equation[J]. Journal of Building Science and Engineering,2012,29(01):1-7.

Li Peng. Durability and life prediction of concrete under load and salt solution coupling [D]. Yangzhou University,2014.