Preparation and Performance of Chitosan-gallic acid/Methacrylic Anhydride Composite Antibacterial Hydrogel

Tianfei Guo; Weijie Sun; Jun Li; Siqin Huang; Guixiang Hou

doi:10.54097/m97g0752

Authors

Tianfei Guo
Weijie Sun
Jun Li
Siqin Huang
Guixiang Hou

DOI:

https://doi.org/10.54097/m97g0752

Keywords:

Chitosan; Gallic Acid; Methacrylic Anhydride; Hydrogels; Antibacterial.

Abstract

Firstly, chitosan-gallic acid derivative (GA-CS) was prepared by reacting chitosan (CS) with gallic acid (GA), which was combined with chitosan (CM) modified by methacrylic anhydride (MA) acylation as an antibacterial modifier, and the composite hydrogel was prepared by light curing. The mechanical properties, swelling rate, surface contact angle, water retention and micromorphology of the hydrogel were tested to explore the effect of GA-CS on the antibacterial effect of the composite hydrogel. The results showed that the compressive strength of the composite hydrogel was 225kPa, and with the addition of the antimicrobial monomer GA-CS, the antibacterial effect and water retention rate of the composite hydrogel increased. However, the surface contact angle with water increased compared with that without GA-CS, and the swelling rate decreased. When the mass ratio of GA-CS to CM was 2:98, the diameter of the inhibition zone increased from 9.85mm to 13.96mm of the pure chitosan sample, the surface contact angle with water was 17.6°, the swelling rate of the sample was 79.32% in 24 hours, and the water content of more than 50% could be maintained for about 7 hours.

Downloads

Download data is not yet available.

References

E. A. Kamoun, E. S. Kenawy, X. Chen. A review on polymeric hydrogel membranes for wound dressing applications: PVA-based hydrogel dressings, J Adv Res, vol. 8(2017) No.3, p. 217-233.

X.L. Zhang, Y. Zhang. Preparation and Characterization of Collagen/O-Carboxymethyl Chitosan Composite Hydrogels, Polymeric Materials Science and Engineering, vol. 36(2021) No.11, p. 139-144.

Q. Zhao, X.Y. Zhao, L. Yan, et al. Study on bilayer composite hydrogel film for wound dressing based on chitosan/sodium alginate-polyvinyl alcohol, Drug Evaluation Research, vol. 46(2023) No.11, p. 2321-2329.

P. Li, X. Yang. Research on the improvement of mechanical properties and antibacterial properties of chitosan hydrogels based on copper ion cross-linking, Beijing Biomedical Engineering, vol. 43(2024) No.1, p. 88-93.

Y.L. Dai, H.Y. Liu, N.H. Song, et al. Construction of antibacterial hydrogel coating on urinary catheters by green biogenic nanoceria, Chemistry, vol. 87(2024) No.4, p. 464-473.

H.Y. Shi, Y.L. Xi. Research progress on the biological activity of gallic acid, Journal of Jilin Medical College, vol. 41(2020) No.2, p. 146-149.

F. Yuan: Study on edible films of chitosan gallic acid derivatives Study on preparation, properties and application in food storage(MS., Henan Institute of Science and Technology, China, 2022).

R.Y. Huang: Novel Hydrogel Wound Dressing with Hemostatic and Antimicrobial Properties Based on Chitosan (MS., Central China Normal University,China,2018).

C. H. Lei, L. S. Yu, W. Jin, et al. Preparation and application of silk fibroin/chitosan composite fiber membrane, Journal of Textile Research, vol.44(2023) No.11, p. 19-26.

S. H. Aswathy, U. Narendrakumar, I. Manjubala. Commercial hydrogels for biomedical applications, Heliyon, vol. 6(2020) No.4, p. e03719.

H. Chopra, S. Bibi, S. Kumar, et al. Preparation and Evaluation of Chitosan/PVA Based Hydrogel Films Loaded with Honey for Wound Healing Application, Interface focus, vol.8 (2022) No.2, p.111.

J. H. Li, S. L. Zhuang. Antibacterial activity of chitosan and its derivatives and their interaction mechanism with bacteria: Current state and perspectives, European Polymer Journal, vol.138(2020) No.9, p.109984.