Analysis and Recommendations on the Cause of Leakage Failure in CT90 Colied Tubing
DOI:
https://doi.org/10.54097/1kft1338Keywords:
Colied tubing; failure analysis; low carbon alloy steel.Abstract
The CT90 coiled tubing experienced leakage during operation. This study aims to investigate the causes of tubing failure, improve its service life, and provide a reference for similar issues. The analysis includes the use of metallographic microscopy, optical microscopy, hardness testing, and other experimental methods to examine the metallographic structure, macro morphology, and hardness of the material. The findings reveal that during the pipeline's use, environmental factors led to brittleness, stress corrosion, crack formation, crack propagation, and subsequent leakage.
Downloads
References
[1] Bi, Z.Y.(2012).Advances in CoiledTubing and lts Application Technology*Welded Pipe*,*35*(9),5-12.DO1:10.19291/i.cnki.1001-3938.2012.09.001
[2] Qiao Lingyun, Li Bofeng, Yan Jixuan, et al. Analysis of Leakage Failure of 110 ksi Grade Coiled Tubing[J]. Welded Pipe and Tube, 2020, 43(03): 45 - 49. DOI: 10.19291/j.cnki.1001 - 3938.2020.03.009
[3] Zhang, F.; Li, J.; Zhu, H.; Jing, C.; Wang, B.; Qi, Y. Study on Variable Stress Corrosion Susceptibility of Four Typical High-Strength Sucker Rods in High-Salinity Well Fluids. [J].Processes 2023, 11(9), 2762. https://doi.org/10.3390/PR11092762.
[4] Kawakami, R.; Saeki, R.; Munetoh, S.; Ohgai, T. Micro-Vickers Hardness of Cu and Cu₂O Dual Phase Composite Films Electrodeposited from Acidic Aqueous Solutions Containing Polyethylene Glycol[J].Crystals 2023, 13(12), 1654. https://doi.org/10.3390/CRYST13121654.
[5] Zhang, P.; Majid, L.; Anthony, E. H.; Marceau, R. K. W.; Hilditch, T.; Tan, M. Y. Effect of Microstructure on Hydrogen Embrittlement and Hydrogen-Induced Cracking Behaviour of a High-Strength Pipeline Steel Weldment[J]Corrosion Science 2024, 227, 111764.https://doi.org/10.1016/J.CORSCI.2023.111764.
[6] Oh, S. B.; Choi, Y.; Shin, E. J.; Seong, B. S. Effect of Hydrogen on HIC and SSC Behaviors of Line Pipe Steels[J]. Proceedings of the Korean Society of Surface Engineering 2013, 556-556.
Downloads
Published
Issue
Section
License
Copyright (c) 2025 Academic Journal of Science and Technology
This work is licensed under a Creative Commons Attribution 4.0 International License.