Analysis of fracture morphology of asphalt concrete under different temperatures

Chunyu Zhang

doi:10.54097/hset.v18i.2654

Authors

Chunyu Zhang

DOI:

https://doi.org/10.54097/hset.v18i.2654

Keywords:

Asphalt concrete, Splitting failure, Bending failure, Fracture morphology

Abstract

By studying the fracture morphology of splitting failure and bending failure of asphalt mixture under different temperatures, it is confirmed that temperature has an impact on the micro mechanism of asphalt mixture fracture. The fracture at low temperature is relatively flat, the fracture of aggregate and asphalt aggregate interface account for a certain proportion, and the failure of asphalt mixture is mainly brittle fracture; With the increase of temperature, the fracture surface becomes rough, and the fracture of asphalt mortar layer is mainly; The addition of rubber powder improves the viscosity of asphalt and the bonding strength of asphalt mortar, greatly improves the fracture ratio of aggregate and interface area, and improves the crack resistance of asphalt mixture; The fracture morphology of asphalt mixture specimen better reflects its mechanical characteristics.

Downloads

Download data is not yet available.

References

Derek H. Fractography observing, measuring and interpreting fracture surface topography, Cambridge University Press, Cambridge, 1999.

Sheikh MZ, Wang Z, Du B et al, Static and dynamic Brazilian disk tests for mechanical characterization of annealed and chemically strengthened glass, Ceram Int, 45(2019)7931-7944.

Deheng Wei,Ryan C.Hurley,Leong HienPoh et al.. The role of particle morphology on concrete fracture behaviour: A meso-scale modelling approach, Cement and Concrete Research, 134(2020)1-17.

Heqian Song. Lunyong Zhang. Hongxian Shen, Morphology and fracture of oxide bifilm defects in nickel-aluminium bronze, Journal Of Materials Research And Technology-Jmr&T, 10(2021)926-934.

Lv YT, Nie B, Wang LQ, Cui HZ, Li L, Wang R, et al, Optimal microstructures on fatigue properties of friction stir processed NiAl bronze alloy and its resistant fatigue crack growth mechanism, Mater Sci Eng A Struct Mater Prop Microstruct Process 771(2020)1385.

Zhen Cui, Sheng Qian, Guimin Zhang,Zhang Maochu, An Experimental Investigation of the Influence of Loading Rate on Rock Tensile Strength and Split Fracture Surface Morphology, Rock Mechanics and Rock Engineering 54(2021)1969-1983.

ZUO Jianping. Fractography of sandstone failure under temperature-tensile stress coupling effects, Chinese Journal of Rock Mechanics and Engineering,12 (2007)2444-2457.

Gong FQ, Zhao GF, Dynamic indirect tensile strength of sandstone under diferent loading rates, Rock Mech Rock Eng, 47(2014)2271-2278.

Li XF, Li X, Li HB et al, Dynamic tensile behaviours of heterogeneous rocks: the grain scale fracturing characteristics on strength and fragmentation, Int J Impact Eng, 118(2018)98-118.

Wang H, Ren C, Wan Y et al, Experimental study on fracture process of sintered Nd-Fe-B magnets during dynamic Brazilian tests, J Magn Magn Mater, 471(2019)200-208.

SHEN Xinpu, FENG Jinlong, DAI Shuhong, PAN Yishan. STUDY ON INFLUENCE OF BOUNDARY CONDITIONS ON RESULTS OF FOUR POINT SHEAR CONCRETE SPEKLES EXPERIMENTS, Chinese Journal of Rock Mechanics and Engineering, 27 (2008) 3528-3534.

Khosravani MR, Silani M, Weinberg K, Fracture studies of ultrahigh performance concrete using dynamic Brazilian tests. Theor Appl Fract Mech, 93(2018)302-310.

Dong Yuguang, Li Huijian, Yan Xiaoli, Analysis of the crack propagation path of concretes under four-point shearload [J]. Actamechancasolidasinic, 25(2004)198-202.

Alekh Bhurke, E. Shin, Lawrence Drzal, Fracture Morphology and Fracture Toughness Measurement of Polymer-Modified Asphalt Concrete,Transportation Research Record, 1590(1997)23-33.

Mo LT, Huurman M, Wu SP, Molenaar AAA, Cao TW. Damage accumulation model for monotonic and dynamic shear fracture of asphalt-stone adhesion. Theor Appl Fract Mech 46(2006)140-147.

Mo LT, Huurman M, Wu SP, Molenaar AAA. Finite element analysis and experimental study on tensile fatigue behavior of asphalt-stone adhesion. Fatigue Fract Eng Mater Struct ,30(2007)823-831.